RESUMO Polyols as solvents are widely and successfully used in various methodologies to obtain zinc oxide nanostructures. One of the main reasons of using polyols is related to its capacity to prevent the agglomeration of ZnO nanoparticles during the synthesis and to promote a more stable colloidal solution of it. In this work it is presented, for the first time, the obtaining of nanostructured ZnO by a polyol mediated solvothermal synthesis using zinc nitrate as precursor. The combination of the zinc source with sodium hydroxide in a polyol medium with PVA as dispersing agent provided a simple process for obtaining nanostructured ZnO. The zinc oxide nanostructures obtained were characterized by UV-visible, XRD, FESEM, TEM, DLS and BET. As result, was obtained a wurtzite phase with hexagonal structure with crystallite size of 12 nm and, according to TEM micrographs, an average size of 14 nm, which was corroborated to other analyses.

Oil is a major pollutant of water resources, affects aquatic life, causing environmental degradation. Currently there is an increase in studies of membrane applied to separation of oil-water. Among these membranes, there are composite membranes, which show as main characteristic an association of organic and inorganic membrane properties. In a tangential flow process, the ceramic tube (support) is responsible for the mechanical strength of the membrane and the selective barrier property of the membrane is established by the polymer. The aim of this work is the application of α-alumina/polyamide 66 composite membrane in the retention of sunflower oil from oil-water emulsions and the study of resistance of such membranes in ultrafiltration processes. The α-alumina ceramic tubes were impregnated internally with a solution of polyamide 66 (PA66) (5% w/v) and tested with distilled water and sunflower oil solutions at concentrations of 50, 100 and 200 mg·L-1. Membranes impregnated with PA66 showed a sunflower oil retention between 53.5 and 99.5% and superior membrane resistance (MR) to the permeate flux (1.92 x 1013 a 5.52 x 1013) which explains the decrease in the permeate volume.

This paper aims the morphological and structural characterization of ceramic membranes of mullite and their application in the removal of Escherichia coli. A complex irregular structure presented by the pores of the membrane was verified by scanning electron microscopy (SEM). The average pore size and distribution were determined by mercury intrusion porosimetry. The average pore size of the material presented was 0,39 µm. Microfiltration tests resulted in a protein retention of 46, 76 and 89% for trypsin (TR), egg albumin (EA) and bovine serum albumin (BSA), proving the efficiency of the membrane microfiltration tests for molecular weight of 69 kDa. The application of the membranes on the retention of gram-negative bacterium E. coliresulted in a 66% efficiency at a pressure of 200 kPa and a 98% efficiency when applied a pressure of 50 kPa. Therefore, the use of mullite membranes show limited efficiency towards bacteria retention. Nevertheless, they present fluxes similar to other materials proposed in the literature.

In this study, polymer/ceramic composite membranes were prepared and characterized. The polymer used was polyamide 66 (PA66) deposited by dip coating on the inner surface of α-alumina-based (Al2O3) microporous tube. A coating on the ceramic support surface and the formation of the selective layer was analyzed by scanning electron microscopy (SEM) in membranes with one (PA-1) and two layers (PA-2). The results of mercury porosimetry showed that the deposition of the polyamide layers decreases the average pore size. The PA-1 presented an average pore size of 0.35 μm, while the PA-2 presented two peaks of 0.18 and 0.56 μm. Both showed a superior performance than the ceramic support (pore diameter of 0.65 μm). Although, the permeate flux was higher with an impregnation membrane, the number of layers (one or two) just introduced a slight difference in pore statistical analysis. The order of rejection coefficient values for protein molecules is BSA > egg albumin > trypsin. The permeation tests showed that the composite membrane can be applied in ultrafiltration processes with MWCO of 69 kDa.